Yıl 2015, Cilt: 15 Sayı: 2, 261 - 266, 09.04.2015
https://doi.org/10.17475/kuofd.34547

Öz

Wood is a preferred important material due to having many advantages for many uses. However, wood is degraded by time under the effects of biotic and abiotic factors. Therefore, wood should be protected from fungi, insects and other climate factors. Among these, heat treatment methods increase the durability of wood properties. Especially, oil heat treatment improves the dimensional stability and color stability in a positive direction. Thus, wood can be used for garden furniture or siding. In this study, water based varnish and paint were applied on oil heat treated scots pine (Pinus sylvestris L.) wood. Effects of oil heat treatment on adhesion strength and hardness of varnish and paint films were determined. Results showed that hardness of varnish layers (38) on oil heat treated scots pine wood is higher than paint layers (25.6)

Kaynakça

  • ASTM D 4366-95., Test Methods for Hardness of Organic Coatings by Pendulum Damping Tests. ASTM International, USA, 2002.
  • ASTM D-3023, Standard Practice for Determination of Resistance of Factory-Applied Coatings on Wood Products to Stains and Reagents. ASTM International, USA, 2011.
  • ASTM D-4541, Standard Test Method for Pull-Off Strength of Coatings Using Portable Adhesion Testers. ASTM International, USA, 2009.
  • Bazyar, B. 2012. Decay resistance and physical properties of oil heat treated aspen wood. BioResources, 7(1), 0696-0705.
  • Dubey, M.K., Pang, S., Walker, J. 2011. Effect of oil heating age on colour and dimensional stability of heat treated Pinus radiata. European Journal of Wood and Wood Products, 69 (2), 255-262.
  • Dubey M.K., Pang, S., Walker, J. 2012. Changes in chemistry, color, dimensional stability and fungal resistance of Pinus radiata D. Don wood with oil heat-treatment, Holzforschung, 66 (1), 49-57.
  • FPInnovations® Forintek Division, Canada, 2008. Coatability of oil-thermal-treated post –MPB Lodgepole pine sapwood.
  • -
  • Hill, C.A.S. 2006, Wood modification chemical thermal and other processes, John Wiley & Sons Pres.
  • Homan W., Tjeerdsma B., Beckers E. Jorissen A. 2000. Structural and other properties of modified wood. World conference on timber engineering. Whistler Resort, British Columbia, Canada July 31 - August 3, 2000.
  • -
  • Jämsä S., Ahola P., Viitaniemi P. 2000. Long-term natural weathering of coated ThermoWood. Pigment & Resin Technology, 29 (2), 68-74.
  • Özkan, O.E. 2013. Isıl işlemle muamele edilmiş göknar odununun biyolojik, mekanik, fiziksel ve dış ortam dayanımı özellikleri. Yüksek Lisans Tezi, Kastamonu Üniversitesi Fen Bilimleri Enstitüsü, 95 s. Kastamonu.
  • Petrič M., Knehtl B., Krause A., Militz H., Pavlič M., Pétrissans M., Gérardin P. 2007. Wettability of waterborne coatings on chemically and thermally modified pine wood. Journal of Coatings Technology and Research, 4 (2), 203-206. DOI 10.1007/s11998-007-9023-2
  • Sidorova E. 2008. Oil heat treatment of wood. Proceedings of the 4th meeting of the Nordic Baltic Network in Wood Material Science & engineering, 13-14 November, Riga, Latvia.
  • Suttie E., Thompson J.H.R. 2001. Opportunites for UK grown timber: Wood Modification State of The Art Review. DTI Contruction Industry Directorate and Forestry Commission, Project Report Number 203-343.
  • Temiz A., Terziev N., Jacobsen B., Eikenes M. 2006. Weathering, water absorption, and durability of silicon, acetylated, and heat-treated wood. Journal of Applied Polymer Science, 102 (5), 4506-4513. DOI:10.1002/app.24878
  • Tomak E.D. ve Yıldız Ü.C. 2010. Odunun kimyasal modifikasyonu. III. Ulusal Karadeniz Ormancılık Kongresi 20-22 Mayıs 2010 Cilt: IV Sayfa: 1681-1690.
  • TS EN 351-1, Ahşap ve Ahşap Esaslı Mamullerin Dayanıklılığı-Emprenye Edilmiş Masif Ahşap-Bölüm 1: Emprenye Maddesinin Nüfuz Derinliği ve Tutulma Miktarının Sınıflandırılması. T.S.E., Ankara 2010.
  • TS EN ISO 4624, Boyalar ve Vernikler - Yapışmanın Tayini İçin Çekme Deneyi. T.S.E., Ankara 2006.
  • TS.2470, Odunda Fiziksel ve Mekaniksel Deneyler İçin Numune Alma Metotları ve Genel Özellikler, T.S.E., Ankara, 1976.
  • URL-1 Yeni Turan Bezir Yağ San. ve Tic. A.Ş. Güvenlik Bilgi Formu. http://www.yenituran.com/urunler/bezir.htm
  • Yildiz S., Yildiz U.C., Tomak E.D. 2011. The effects of natural weathering on the properties of heat treated alder wood. BioRes., 6 (3), 2504-2.

Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri

Yıl 2015, Cilt: 15 Sayı: 2, 261 - 266, 09.04.2015
https://doi.org/10.17475/kuofd.34547

Öz

Ahşap sahip olduğu bazı iyi avantajları sayesinde birçok kullanım yerinde tercih edilen önemli bir malzemedir. Ancak, biyotik ve abiyotik faktörlerin zaman içerisindeki etkisiyle ahşapta bazı bozulmalar görülmektedir. Bu yüzden, ahşabın mantar, böcek ve diğer iklim koşullarının etkilerinden bazı yöntemler ile korunması gerekmektedir. Örneğin, ısıl işlem ahşabın bazı özelliklerini olumlu yönde artırmaktadır. Özellikle, yağlı ısıl işlemin ahşabın boyutsal kararlılığı ve renk kararlılığını iyileştirdiği görülmektedir. Bu sayede ahşap, bahçe mobilyalarında ya da dış cephe kaplamalarında kullanılabilmektedir.

Bu çalışmada, bezir yağı ile ısıl işlem görmüş sarıçam (Pinus sylvestris L.) odunlarından hazırlanan deney numunelerine, su bazlı vernik ve su bazlı boya tatbik edilerek, yapışma ve sertlik performansları belirlenmiştir. Araştırma sonuçlarına göre, bezir yağı ile ısıl işlem gören sarıçam odunlarında, vernik katmanı sertlik değerleri, boya katmanı sertlik değerlerinden yüksek çıkmıştır.

Kaynakça

  • ASTM D 4366-95., Test Methods for Hardness of Organic Coatings by Pendulum Damping Tests. ASTM International, USA, 2002.
  • ASTM D-3023, Standard Practice for Determination of Resistance of Factory-Applied Coatings on Wood Products to Stains and Reagents. ASTM International, USA, 2011.
  • ASTM D-4541, Standard Test Method for Pull-Off Strength of Coatings Using Portable Adhesion Testers. ASTM International, USA, 2009.
  • Bazyar, B. 2012. Decay resistance and physical properties of oil heat treated aspen wood. BioResources, 7(1), 0696-0705.
  • Dubey, M.K., Pang, S., Walker, J. 2011. Effect of oil heating age on colour and dimensional stability of heat treated Pinus radiata. European Journal of Wood and Wood Products, 69 (2), 255-262.
  • Dubey M.K., Pang, S., Walker, J. 2012. Changes in chemistry, color, dimensional stability and fungal resistance of Pinus radiata D. Don wood with oil heat-treatment, Holzforschung, 66 (1), 49-57.
  • FPInnovations® Forintek Division, Canada, 2008. Coatability of oil-thermal-treated post –MPB Lodgepole pine sapwood.
  • -
  • Hill, C.A.S. 2006, Wood modification chemical thermal and other processes, John Wiley & Sons Pres.
  • Homan W., Tjeerdsma B., Beckers E. Jorissen A. 2000. Structural and other properties of modified wood. World conference on timber engineering. Whistler Resort, British Columbia, Canada July 31 - August 3, 2000.
  • -
  • Jämsä S., Ahola P., Viitaniemi P. 2000. Long-term natural weathering of coated ThermoWood. Pigment & Resin Technology, 29 (2), 68-74.
  • Özkan, O.E. 2013. Isıl işlemle muamele edilmiş göknar odununun biyolojik, mekanik, fiziksel ve dış ortam dayanımı özellikleri. Yüksek Lisans Tezi, Kastamonu Üniversitesi Fen Bilimleri Enstitüsü, 95 s. Kastamonu.
  • Petrič M., Knehtl B., Krause A., Militz H., Pavlič M., Pétrissans M., Gérardin P. 2007. Wettability of waterborne coatings on chemically and thermally modified pine wood. Journal of Coatings Technology and Research, 4 (2), 203-206. DOI 10.1007/s11998-007-9023-2
  • Sidorova E. 2008. Oil heat treatment of wood. Proceedings of the 4th meeting of the Nordic Baltic Network in Wood Material Science & engineering, 13-14 November, Riga, Latvia.
  • Suttie E., Thompson J.H.R. 2001. Opportunites for UK grown timber: Wood Modification State of The Art Review. DTI Contruction Industry Directorate and Forestry Commission, Project Report Number 203-343.
  • Temiz A., Terziev N., Jacobsen B., Eikenes M. 2006. Weathering, water absorption, and durability of silicon, acetylated, and heat-treated wood. Journal of Applied Polymer Science, 102 (5), 4506-4513. DOI:10.1002/app.24878
  • Tomak E.D. ve Yıldız Ü.C. 2010. Odunun kimyasal modifikasyonu. III. Ulusal Karadeniz Ormancılık Kongresi 20-22 Mayıs 2010 Cilt: IV Sayfa: 1681-1690.
  • TS EN 351-1, Ahşap ve Ahşap Esaslı Mamullerin Dayanıklılığı-Emprenye Edilmiş Masif Ahşap-Bölüm 1: Emprenye Maddesinin Nüfuz Derinliği ve Tutulma Miktarının Sınıflandırılması. T.S.E., Ankara 2010.
  • TS EN ISO 4624, Boyalar ve Vernikler - Yapışmanın Tayini İçin Çekme Deneyi. T.S.E., Ankara 2006.
  • TS.2470, Odunda Fiziksel ve Mekaniksel Deneyler İçin Numune Alma Metotları ve Genel Özellikler, T.S.E., Ankara, 1976.
  • URL-1 Yeni Turan Bezir Yağ San. ve Tic. A.Ş. Güvenlik Bilgi Formu. http://www.yenituran.com/urunler/bezir.htm
  • Yildiz S., Yildiz U.C., Tomak E.D. 2011. The effects of natural weathering on the properties of heat treated alder wood. BioRes., 6 (3), 2504-2.
Toplam 23 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Makaleler
Yazarlar

Hacı Kesik

Hasan Vurdu

Kubulay Çağatay

Osman Özkan

Mustafa Öncel Bu kişi benim

Yayımlanma Tarihi 9 Nisan 2015
Yayımlandığı Sayı Yıl 2015 Cilt: 15 Sayı: 2

Kaynak Göster

APA Kesik, H., Vurdu, H., Çağatay, K., Özkan, O., vd. (2015). Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri. Kastamonu University Journal of Forestry Faculty, 15(2), 261-266. https://doi.org/10.17475/kuofd.34547
AMA Kesik H, Vurdu H, Çağatay K, Özkan O, Öncel M. Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri. Kastamonu University Journal of Forestry Faculty. Kasım 2015;15(2):261-266. doi:10.17475/kuofd.34547
Chicago Kesik, Hacı, Hasan Vurdu, Kubulay Çağatay, Osman Özkan, ve Mustafa Öncel. “Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma Ve Sertlik Özellikleri”. Kastamonu University Journal of Forestry Faculty 15, sy. 2 (Kasım 2015): 261-66. https://doi.org/10.17475/kuofd.34547.
EndNote Kesik H, Vurdu H, Çağatay K, Özkan O, Öncel M (01 Kasım 2015) Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri. Kastamonu University Journal of Forestry Faculty 15 2 261–266.
IEEE H. Kesik, H. Vurdu, K. Çağatay, O. Özkan, ve M. Öncel, “Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri”, Kastamonu University Journal of Forestry Faculty, c. 15, sy. 2, ss. 261–266, 2015, doi: 10.17475/kuofd.34547.
ISNAD Kesik, Hacı vd. “Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma Ve Sertlik Özellikleri”. Kastamonu University Journal of Forestry Faculty 15/2 (Kasım 2015), 261-266. https://doi.org/10.17475/kuofd.34547.
JAMA Kesik H, Vurdu H, Çağatay K, Özkan O, Öncel M. Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri. Kastamonu University Journal of Forestry Faculty. 2015;15:261–266.
MLA Kesik, Hacı vd. “Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma Ve Sertlik Özellikleri”. Kastamonu University Journal of Forestry Faculty, c. 15, sy. 2, 2015, ss. 261-6, doi:10.17475/kuofd.34547.
Vancouver Kesik H, Vurdu H, Çağatay K, Özkan O, Öncel M. Yağlı Isıl İşlem Görmüş Sarıçam Odunlarında Koruyucu Katmanın Yapışma ve Sertlik Özellikleri. Kastamonu University Journal of Forestry Faculty. 2015;15(2):261-6.

14178  14179       14165           14166           14167            14168